Backed by rich industry experience, we are also matching up with the demands of Brass Strips. Extensively demanded by various industries, these strips are available in various dimensions, specifications and sizes as per the requirements of our clients. Manufactured using the optimum-grade raw material, our offered products are closely tested on various parameters.

Some of the features of this product:

With the aid of our sophisticated infrastructure facility, we are able to cater to the variegated requirements of our clients by offering Aluminum Alloy 2219. Extensively used in the manufacturing of structural components, these products are suitable for high temperature applications as well as high strength weldments. Further, the alloy 2219 offered by us is manufactured in adherence with the industry set standards.

Aluminum 2219: Gings, Fasteners Etc.

The following Other details of cover Aluminum 2219:

• AMS 4066
• AMS 4068
• ASTM B209
• ASTM B211
• ASTM B221
• ASTM B241 (Pipe- Seamless)
• ASTM B247 (Forging - Open Die)
• ASTM B316
• MIL A-46118
• MIL A-46808
• MIL A-8920 (plate)
• SAE J454
• UNS A92219
• QQ A-250
• QQ A-367 (Forging - Open Die)
• QQ A-430

Kindly send your inquiries to
sales@maharashtrametal.co.in

Principal design features:

• AL 2219 is an age-hardenable copper containing alloy of aluminum

Applications:

• Commonly used in the manufacture of structural components
• Used in high temperature applications as well as high strength weldments

Machinability:

• In the annealed condition this alloy is readily machined

Forming:

• The alloy may be readily formed by conventional methods

Welding:

• Welding heat input affects the corrosion resistance of this alloy in an adverse manner

Heat treatment:

• Solution heat treatment is done at 1000 F
• Followed by a cold water quench (T4 condition)

Forging:

• Hot forging may be done providing the finished product is given
• The aging heat treatment to restore corrosion resistance

Hot working:

• Hot working should be avoided unless it is feasible to give the finished product
• the aging heat treatment after all hot working is done

Cold working:

• Cold working by conventional means is readily accomplished

Annealing:

• Solution annealing is done at 1000 F for adequate time to allow thorough heating, followed by a cold water quench

Hardening:

• This alloy is hardened (strengthened) by an aging heat treatment
• By controlled cold working from the solution annealed condition

Other Physical Props:

• Electrical conductivity 30% that of copper